Product Detailed
Related Categories:Aluminum Composite Panels
Related Product Searches:mirror aluminium composite panel,High Quality mirror aluminium composite panel,mirror aluminium composite panel IDEABOND
mirror aluminium composite panel
1.excellent in quality.
2.mulriple color.
3.superior strength.
4.durablity&fire resistant
Related Product Searches:mirror aluminium composite panel,High Quality mirror aluminium composite panel,mirror aluminium composite panel IDEABOND
mirror aluminium composite panel
1) Standard:
2) Constitution Structure:
· Top Coating Polyester/PVDF · Aluminum skin · Macromolecular lamination film · Nontoxic polyethylene core or No-combustible filled core · Macromolecular lamination film · Aluminum skin · Service coating or mill finished
3) Specification:
Standard size:
Item | Total Thickness(mm) | ALU thickness(mm) | Width(mm) | Length(mm) | Color |
Standard | 4 | 0.5 | 1220 | 2440 | Refer to color chart |
Option | 3, 5, 6 | 0.12~0.5 | 900 ≤ W ≤ 1600 | Customized |
Fire behavior:
TESTING ITEMS | TEST CONDITION | RESULT | CONCLUSION | STANDARD |
Fire safety test | BS 476:Part 6:1989 | Total fire progagation index:0.05 | CLASS 0 | BS 476:Part 6:1989 |
Fire safety test | Relative Humidity of 50±10°F | Flame spread at 1.5 min:60mm | CLASS 1 | BS 476:Part 7:1997 |
Temperature of 23±2°C | Final flame spread:60mm | |||
Fire safety test | Relative Humidity of 50±5°F | Flame spread index:10 | CLASS A | ASTM E-84-04 |
Temperature of 73±2°F | Smoke developed value:15 |
General technical data:
Testing items | Result | Testing items | Result | Testing items | Result | |
Apprearance quality | Vesige | Indistinct | Weight | t4mm=5.7kg/SQM | Finish coating thickness | 30±5μm |
Coating omit | No | Outdoor temperature | No abnormity | Gloss tolerance | 4.3(gloss56.8) | |
Ripples | No | Thermal expansion | 1.59×10³°C-1 | Pencil hardness | 3H | |
Flaw | No | Deflection temperature | 105°C | Toughness(T-bend) | 2T no rift | |
Abrasion | No | Thermal conductivity | 0.102kcal/mhr°C | Coating adhesive force | Class 1 (4B) | |
Scratch | No | Flexural rigidity | 14.0×10³ | Impact resistance(50kg.cm) | no depainting, no crack | |
Aberration | Indistinct | Penetrating resistance | 9.0kn | Grinding resistance | 7.4L/μm | |
180°peel strength | 9.117N/mm | Mortar resistance | 24 Hrs Pat test exceed | |||
Dimensions deviation | Length | 0~+0.4mm | Acoustic insulation | 25dB | Humidity resistance | 3000hrs no blister |
Width | 0~+0.6mm | Bending dlastic modulus | 2.8×104Pa | Boiling-water resistance | No change | |
Thickness | –0.02~0mm | Shearing resistance | 28.6MPa | Salt-spray resistance | 3000hrs no blister | |
Diagonals windage | 1.7mm | Fire propagation | Qualified | Acid resistance | No change | |
Edge unstraightness | 0.4mm/m | Wind-pressure resistance | Passed | Alkali resistance | Pssed | |
Warpage | 2.0mm/m | Properties angainst water | Passed | Solvent resistance | Pssed | |
Properties angainst air | Passed | Color retention | E<5 | |||
Bending strength | 112MPa | Chalk resistance | Max value:8unit | |||
Minimum bending redius | =300mm | Gloss retention | 90% |
4)Application:
5) Factory Facilities:
6)Packages:
Package in bulk:
Package in wooden case: